EVALUATION OF PROPERTIES OF BITUMEN MODIFIED WITH WASTE TYRE
DOI:
https://doi.org/10.4314/njt.331.757Keywords:
Bitumen, Waste Tyre, Penetration, Softening Point, Viscosity, DuctilityAbstract
The research investigates the properties of bitumen modified with used tyre. Basic tests such as penetration, softening point, viscosity , flash and fire point and ductility test were carried out by using shredded waste tyre which varied from 0% to 20% by weight of 60/70 penetration grade bitumen at 1600C using dry mix method. Penetration value decreased with addition of 20% tyre while increase in softening point, viscosity, flash and fire point were obtained with the corresponding values of 80.90C, 250.96 sec and 189/280.120C respectively. However, the values obtained exceeded the minimum values specified by American Standard for Testing and Materials (ASTM). The ductility value obtained with the addition of 6% and 14% tyre are 44.64cm and 40.6cm respectively. Thus, addition of 6% tyre content to bitumen is however suggested for best ductility value.
Downloads
Issue
Section
License
The contents of the articles are the sole opinion of the author(s) and not of NIJOTECH.
NIJOTECH allows open access for distribution of the published articles in any media so long as whole (not part) of articles are distributed.
A copyright and statement of originality documents will need to be filled out clearly and signed prior to publication of an accepted article. The Copyright form can be downloaded from http://nijotech.com/downloads/COPYRIGHT%20FORM.pdf while the Statement of Originality is in http://nijotech.com/downloads/Statement%20of%20Originality.pdf
For articles that were developed from funded research, a clear acknowledgement of such support should be mentioned in the article with relevant references. Authors are expected to provide complete information on the sponsorship and intellectual property rights of the article together with all exceptions.
It is forbidden to publish the same research report in more than one journal.