INFLUENCE OF IRON CONTENT AND PLASTIC DEFORMATION ON THE MECHANICAL PROPERTIES OF 8011-TYPE Al-Fe-Si ALLOY
DOI:
https://doi.org/10.4314/njt.351.1058Keywords:
aluminium, iron, Mechanical properties, UTS, percentage deformationAbstract
This paper examines the effect of iron content and plastic deformation on the mechanical properties of wrought Al-Fe-Si alloy. Seven samples each of dimension 240mm x 140mm x 7mm were cast for each aluminium alloy plate containing iron content of 0.708%, 0.909% and 0.931% by chill casting method. As-received commercial aluminium alloy 8011 has an iron content of 0.857% and it was cut into seven samples of the same geometry. Cold rolling experiment was carried out from 30% to 80% reduction in thickness. The mechanical properties of the alloys were investigated. The results showed that the maximum ultimate tensile strength obtained for alloys 0.708%Fe and 0.857%Fe were 171.45MPa and176.45MPa respectively both occurred at 60% reduction in thickness while alloys 0.909%Fe and 0.931%Fe respectively have 163.16MPa and 170.00MPa at 80% reduction in thickness. An increase in iron content led to corresponding decrease in tensile strength but at 80% reduction in thickness, the strength increase with iron content for alloys of 0.9%Fe and above. The micro-vicker hardness values increases, reaching the peak and then decreases with increasing percentage deformation.
Downloads
Issue
Section
License
The contents of the articles are the sole opinion of the author(s) and not of NIJOTECH.
NIJOTECH allows open access for distribution of the published articles in any media so long as whole (not part) of articles are distributed.
A copyright and statement of originality documents will need to be filled out clearly and signed prior to publication of an accepted article. The Copyright form can be downloaded from http://nijotech.com/downloads/COPYRIGHT%20FORM.pdf while the Statement of Originality is in http://nijotech.com/downloads/Statement%20of%20Originality.pdf
For articles that were developed from funded research, a clear acknowledgement of such support should be mentioned in the article with relevant references. Authors are expected to provide complete information on the sponsorship and intellectual property rights of the article together with all exceptions.
It is forbidden to publish the same research report in more than one journal.
How to Cite