SCANNING SPEED INFLUENCE ON THE PHYSICAL PROPERTIES OF LASER METAL DEPOSITION TITANIUM ALLOY
DOI:
https://doi.org/10.4314/njt.361.1222Keywords:
Additive manufacturing, Laser metal deposition (LMD), Material efficiency, Titanium alloyAbstract
The most commonly used aerospace titanium alloy, Ti6Al4V, was deposited on Ti6Al4V plate of dimension 72 x 72 x5mm. The laser power of 3 kW, powder flow rate of 1.44 g/min and gas flow rate of 4 l/min were used throughout the deposition process. The transverse/ scanning speed was varied between 0.005 to 0.095 m/sec according to established result of the preliminary study that produces full dense and pore free deposits. The mass of the deposited powder was obtained by weighing the substrate before the deposition and reweighing after the deposition. The substrate and the deposits were thoroughly cleaned using wire brush and acetone to remove unmelted powder particles from the surface of the substrate and the deposit. The height and width of the deposits were measured with Venier Caliper and the material efficiencies were determined using developed equations. The objective of this research is to determine the influence of the scanning speed on the material efficiency and deposit height in laser metal deposition of titanium alloy- Ti6Al4V. The results of this study showed that, for the set of processing parameter used in this study, the optimum scanning speed was at 0.015 m/sec with the optimum material utilization efficiency of 83.33% and the deposition height of 1.09 mm.
Downloads
Issue
Section
License
The contents of the articles are the sole opinion of the author(s) and not of NIJOTECH.
NIJOTECH allows open access for distribution of the published articles in any media so long as whole (not part) of articles are distributed.
A copyright and statement of originality documents will need to be filled out clearly and signed prior to publication of an accepted article. The Copyright form can be downloaded from http://nijotech.com/downloads/COPYRIGHT%20FORM.pdf while the Statement of Originality is in http://nijotech.com/downloads/Statement%20of%20Originality.pdf
For articles that were developed from funded research, a clear acknowledgement of such support should be mentioned in the article with relevant references. Authors are expected to provide complete information on the sponsorship and intellectual property rights of the article together with all exceptions.
It is forbidden to publish the same research report in more than one journal.
How to Cite