OPTIMIZATION OF WELD STRENGTH PROPERTIES OF TUNGSTEN INERT GAS MILD STEEL WELDS USING THE RESPONSE SURFACE METHODOLOGY
DOI:
https://doi.org/10.4314/njt.372.1671Keywords:
welding, gas tungten arc welding, tensile strength, hardness, response surface methodologyAbstract
The rise in the failure of mechanical components, some of which are attributable to poor weld joints has given rise to research study on the optimization of weld joint strengths. The quality of welds is highly dependent on the right combination of input process parameters. Irrespective of the welding process, the need for the right combination of input process parameters cannot be over emphasized. To achieve a desired weld quality, the weld features such bead geometry and the mechanical properties were examined and related to the weld input parameters. The Response Surface Methodology (RSM) was used to predict and optimize the weld strength properties (tensile strength and hardness) of a Gas Tungsten Arc Welded 10mm thick mild steel plate. Model adequacy checks, was done using analysis of variance (ANOVA) and found to be adequate. The ANOVA showed that current and gas flow rate had the most significant effect on the tensile strength, but on the Hardness, the gas flow rate and filler rod had the most significant effect. The model F-value of 12.69 at a P value of 0.0001 for the tensile strength and F-value of 8.51 at a P value of 0.0001 for the hardness, showed the significance of the model employed. The optimal tensile strength of 497.555N/mm2 and Hardness of 192.556BHN was observed at a current of 170.12 amp, voltage of 19.84 volt, gas flow rate of 23.92 l/min and filler rod diameter of 2.4mm.
Published
Issue
Section
License
The contents of the articles are the sole opinion of the author(s) and not of NIJOTECH.
NIJOTECH allows open access for distribution of the published articles in any media so long as whole (not part) of articles are distributed.
A copyright and statement of originality documents will need to be filled out clearly and signed prior to publication of an accepted article. The Copyright form can be downloaded from http://nijotech.com/downloads/COPYRIGHT%20FORM.pdf while the Statement of Originality is in http://nijotech.com/downloads/Statement%20of%20Originality.pdf
For articles that were developed from funded research, a clear acknowledgement of such support should be mentioned in the article with relevant references. Authors are expected to provide complete information on the sponsorship and intellectual property rights of the article together with all exceptions.
It is forbidden to publish the same research report in more than one journal.
How to Cite