MECHANICAL PROPERTIES OF ALUMINUM FOAM REINFORCED WITH RECYCLED CERAMIC AGGREGATES
Keywords:
Aluminum Alloy Powder, Digital Image Correlation, Mechanical Properties, Novel Composites, Powder Metallurgy, Recycled Ballistic Aggregates.Abstract
This research work investigates the mechanical properties of two distinct novel composites of aluminum foam made from the addition of recycled ballistic aggregates to the foams of aluminum alloy powder in regular and random patterns through powder metallurgy process. The mechanical attributes of these composites were examined in compression loading using digital image correlation (DIC) and compared to baseline properties of steel and aluminum foams obtained in the laboratory and literature respectively. The results obtained for aluminum foam ceramic composite made through the dispersion of ceramic aggregates in regular orientation showed an increase in its plateau stress, yield strength, strength/density ratio and relative density, but a decrease in its modulus of elasticity was observed. This observation was similar to the composite with a random arrangement of ceramic aggregates, except for a decrease noticed in its yield strength and elastic modulus.
Downloads
Published
Issue
Section
License
The contents of the articles are the sole opinion of the author(s) and not of NIJOTECH.
NIJOTECH allows open access for distribution of the published articles in any media so long as whole (not part) of articles are distributed.
A copyright and statement of originality documents will need to be filled out clearly and signed prior to publication of an accepted article. The Copyright form can be downloaded from http://nijotech.com/downloads/COPYRIGHT%20FORM.pdf while the Statement of Originality is in http://nijotech.com/downloads/Statement%20of%20Originality.pdf
For articles that were developed from funded research, a clear acknowledgement of such support should be mentioned in the article with relevant references. Authors are expected to provide complete information on the sponsorship and intellectual property rights of the article together with all exceptions.
It is forbidden to publish the same research report in more than one journal.